RESUMO
Bone mechanics is well understood at every length scale except the nano-level. We aimed to investigate the relationship between bone nanoscale and tissue-level mechanics experimentally. We tested two hypotheses: (1) nanoscale strains were lower in hip fracture patients versus controls, and (2) nanoscale mineral and fibril strains were inversely correlated with aging and fracture. A cross-sectional sample of trabecular bone sections was prepared from the proximal femora of two human donor groups (aged 44-94 years): an aging non-fracture control group (n = 17) and a hip-fracture group (n = 20). Tissue, fibril, and mineral strain were measured simultaneously using synchrotron X-ray diffraction during tensile load to failure, then compared between groups using unpaired t-tests and correlated with age using Pearson's correlation. Controls exhibited significantly greater peak tissue, mineral, and fibril strains than the hip fracture (all p < 0.05). Age was associated with a decrease in peak tissue (p = 0.099) and mineral (p = 0.004) strain, but not fibril strain (p = 0.260). Overall, hip fracture and aging were associated with changes in the nanoscale strain that are reflected at the tissue level. Data must be interpreted within the limitations of the observational cross-sectional study design, so we propose two new hypotheses on the importance of nanomechanics. (1) Hip fracture risk is increased by low tissue strain, which can be caused by low collagen or mineral strain. (2) Age-related loss of tissue strain is dependent on the loss of mineral but not fibril strain. Novel insights into bone nano- and tissue-level mechanics could provide a platform for the development of bone health diagnostics and interventions based on failure mechanisms from the nanoscale up.
RESUMO
PURPOSE OF REVIEW: Bone matrix exhibits great complexity in its composition, structure and mechanics. Here, we provide a review of recent research articles and appraise the evidence that bone matrix quality is clinically important and possibly targetable for fracture prevention. RECENT FINDINGS: Deformation of mineralised collagen fibrils determines bone fracture mechanics. Slipping and separation at the mineral-fibril and fibril-fibril interfaces, respectively, are the structural mechanisms for plastic deformation and microcrack nucleation. Existing technologies for assessing bone tissue in vivo cannot measure matrix structure or fracture mechanics but have shown limited use in clinical settings for identifying fragility or following treatment outcomes based on composition. Matrix is biomechanically and clinically important, but the knowledge has not translated into clinical practice. The structural mechanisms by which a load is transferred from mineralised collagen fibrils to the whole bone via microcracking have been proven too complex to measure in vivo. The mineral-fibril or fibril-fibril interfaces might be suitable targets for diagnosing fragility or delivering molecules that reduce fracture risk by strengthening the mineral bonds while maintaining flexibility in the fibrils.